小直径单芯液晶聚合物挤塑光缆抗张强度的影响因素分析

詹祎民, 彭峰, 张帆, 强伟, 张栓民, 王小婷, 曹战民

詹祎民, 彭峰, 张帆, 强伟, 张栓民, 王小婷, 曹战民. 小直径单芯液晶聚合物挤塑光缆抗张强度的影响因素分析[J]. 应用光学, 2013, 34(2): 381-384.
引用本文: 詹祎民, 彭峰, 张帆, 强伟, 张栓民, 王小婷, 曹战民. 小直径单芯液晶聚合物挤塑光缆抗张强度的影响因素分析[J]. 应用光学, 2013, 34(2): 381-384.
ZHAN Yi-min, PENG Feng, ZHANG Fan, QIANG Wei, ZHANG Shuan-min, WANG Xiao-ting, CAO Zhan-min. Influence factors for tensile strength of small-diameter liquid-crystalpolymer extruded single-core fiber cable[J]. Journal of Applied Optics, 2013, 34(2): 381-384.
Citation: ZHAN Yi-min, PENG Feng, ZHANG Fan, QIANG Wei, ZHANG Shuan-min, WANG Xiao-ting, CAO Zhan-min. Influence factors for tensile strength of small-diameter liquid-crystalpolymer extruded single-core fiber cable[J]. Journal of Applied Optics, 2013, 34(2): 381-384.

小直径单芯液晶聚合物挤塑光缆抗张强度的影响因素分析

详细信息
    通讯作者:

    詹祎民(1966-),男,陕西户县人,高级工程师,主要从事特种光纤光缆技术研究工作。 Email: jinhuazhanwei@163.com

  • 中图分类号: TN205

Influence factors for tensile strength of small-diameter liquid-crystalpolymer extruded single-core fiber cable

  • 摘要: 从理论上分析了0.5 mm以下小直径单芯液晶聚合物(LCP)光缆在成型过程中,影响光缆抗张强度的主要因素,这些因素主要包括熔融液晶聚合物的温度特性、模芯和模套的结构参数、模芯与模套之间的距离以及光纤的放线张力及其牵引速度等,介绍了各影响因素与光缆抗张强度之间的相互关系,深入分析了光缆加强层厚度与其抗张强度系数之间的相互关系。实验结果证明:小直径液晶聚合物抗张强度与其加强厚度并不存在理想的线性关系,且在一定直径范围内,小直径液晶聚合物光缆具有相同数值的最大抗张强度。
    Abstract: This paper theoretically analyzed main factors of tensile strength of liquid-crystal po-lymer (LCP) extruded single-core fiber cable with the diameter of 0.5 mm during the forming process. The factors mainly contained temperature feature of the melted LCP, structure parameters of mold core and die sleeve, space between die sleeve and mold core, and tension stringing and traction speed of optical fiber. Results show linear relationship between tensile strength and strengthened story thickness of small-diameter LCP is not ideal. The liquid-crystal polymer extruded fiber cable has maximum tensile strength within a certain diameter.
  • [1]曹维敏,林波. LCP料断裂伸长率的改进及其在光纤护层中的应用[J]. 光纤与电缆及其应用技术, 1992, 8(4): 56-62.
    CAO Wei-min, LIN Bo. Improvement of LCP break elongation and its application in optical fiber coating[J]. Optical Fiber & Electric Cable and Their Applications, 1992, 8(4): 56-62. (in Chinese with an English abstract)
    [2]WILEY J. Production of ultrahigh-modulus liquid-crystal polymer rods[J]. Journal of Polymer Science Part B: Polymer Physics, 1988, 26(2): 1549-1552.
    [3]詹祎民,张栓民,彭峰,等. 液晶聚合物小直径光缆挤塑工艺研究[J]. 应用光学, 2008, 29(6): 999-1003.
    ZHAN Yi-min, ZHANG Shuan-min, PENG Feng, et al. Extrusion process for small-diameter fiber cable made of liquid-crystal polymer[J]. Journal of Applied Optics, 2008, 29(6): 999-1003. (in Chinese with an English abstract)
    [4]BOLES D, CAKMAK M, YALCIN B. A multi-stream flow technique to obtain isotropic texture in extruded thermotropic liquid crystalline polymer melts[J]. Polymer Engineering and Science, 2009, 51(4): 73-80.

    [5]BAIRD D G. Conceots in rheological studies of polymeric liquid crystals[M]. New York: Plenum Press, 2005.
    [6]CHUNG T S. Applied science of liquid crystal polymer[J]. Journal of Polymer Science, 1986, 7(2): 1311-1318.
    [7]CHUNG T S. Thermotropic liquid crystal polymers: thin film polymerization, characteristion, blencls and applications[M]. Lancaster, PA: Crcpress Thchnomic, 2001.
    [8]WARD I M. Developments of oriented polymers-2[J]. Elsevier Applied Science, 1987, 80(6): 1230-1236.
    [9]KRIGDUAM W R, LIU C K, YANG D K. Characteristic of thermotropic liquid crystalline polymer[J]. Journal of Polymer Science B: Polymer Physics, 1988, 7(4): 1052-1059.
    [10]ZACHARIADES A E, PORTER R S. The strength and stiffness of polymers[M]. New York: Marcel Dekker, 1983.
计量
  • 文章访问数:  1967
  • HTML全文浏览量:  91
  • PDF下载量:  322
  • 被引次数: 0
出版历程
  • 刊出日期:  2013-03-14

目录

    /

    返回文章
    返回